MULTI PLASTIC FILLER: 0RS008-0.5KG, 0RS008-1KG
Characteristics:
Multifunctional filler with very high flexibility mainly intended for plastic substrates, including polypropylene. Easy to apply and model. It has the properties of both filling and finishing putty. Provides high-quality coating after mechanical processing, does not leave holes or pores. It shows very good adhesion also to metal surfaces (steel, galvanized steel, aluminum) and polyester laminates.
Usage:
The repaired substrate must be clean, dry, degreased, and matted. Thoroughly mix the filler mass with the hardener in an amount of 2-3% by weight, then apply to the substrate for about 3 - 5 min. at 20 °C – higher temperature shortens the product's life and accelerates the curing process.
WARNING: Overdosing the hardener may cause discoloration of the topcoat. It is not recommended to use the product at temperatures below 15 oC. Do not apply directly on reactive primers and one-component acrylic products.
Opis izdelka
MULTI PLASTIC FILLER: 0RS008-0.5KG, 0RS008-1KG
Characteristics:
Multifunctional filler with very high flexibility mainly intended for plastic substrates, including polypropylene. Easy to apply and model. It has the properties of both filling and finishing putty. Provides high-quality coating after mechanical processing, does not leave holes or pores. It shows very good adhesion also to metal surfaces (steel, galvanized steel, aluminum) and polyester laminates.
Usage:
The repaired substrate must be clean, dry, degreased, and matted. Thoroughly mix the filler mass with the hardener in an amount of 2-3% by weight, then apply to the substrate for about 3 - 5 min. at 20 °C – higher temperature shortens the product's life and accelerates the curing process.
WARNING: Overdosing the hardener may cause discoloration of the topcoat. It is not recommended to use the product at temperatures below 15 oC. Do not apply directly on reactive primers and one-component acrylic products.